Bormashenko, Edward; Pogreb, Roman; Sutovski, Semion; Shulzinger, Alexander; Sheshnev, Avigdor; Izakson, Gregory; Katzir, Abraham
Synthetic metals, 01/2004, Letnik: 140, Številka: 1Journal Article
The use of polyaniline emeraldine base films as antireflection coating for near and middle IR optics elements was studied. The optical quality of ZnSe substrates spin-coated with thin PANI EB layers were studied using a Linnik interferometer. The spectral properties of PANI coated ZnSe plates were investigated with FTIR spectrometer. It was shown that PANI coating allows a significant decrease of Fresnel losses in the near and middle IR bands (1.0–6.25 μm). The coating allowed continuous transmission of high power density (up to 3 W/mm 2) of IR radiation produced by CO 2 laser. The laser irradiation damage threshold of the PANI EB coating was studied at a wavelength of 1.5 μm. Microhardness of the coated ZnSe is established as satisfactory.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.