Trunec, Martin; Chlup, Zdenek
Scripta materialia, 07/2009, Letnik: 61, Številka: 1Journal Article
Fracture toughness of nanocrystalline zirconia ceramic stabilized with 1.5 mol.% Y 2O 3 was measured and compared with fracture toughness of submicrometer-grained zirconia ceramics stabilized with 3 mol.% Y 2O 3. It was found that nanocrystalline ceramics demonstrated higher fracture toughness than submicrometer-grained zirconia ceramics with both optimized and common grain sizes. The high fracture toughness of nanocrystalline zirconia was confirmed by two different testing methods: indentation method (15.5 MPa m 0.5) and chevron notched beam method (7.9 MPa m 0.5).
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.