Rivera, O.G.; Allison, P.G.; Jordon, J.B.; Rodriguez, O.L.; Brewer, L.N.; McClelland, Z.; Whittington, W.R.; Francis, D.; Su, J.; Martens, R.L.; Hardwick, N.
Materials science & engineering. A, Structural materials : properties, microstructure and processing, 05/2017, Letnik: 694Journal Article
Here we introduce a novel thermo-mechanical Solid State Additive Manufacturing (SSAM) process referred to as Additive Friction Stir (AFS) manufacturing that provides a new and alternative path to fusion-based additive manufacturing processes for developing fully-dense, near-net shape components with a refined-equiaxed grain morphology. This study is the first to investigate the beneficial grain refinement and densification produced by AFS in IN625 that results in advantageous mechanical properties (YS, UTS, εf) at both quasi-static and high strain rate. Electron Backscatter Diffraction (EBSD) observed grain refinement during the layer deposition in the AFS specimens, where the results identified fine equiaxed grain structures with even finer grain structures forming at the layer interfaces. The EBSD quantified grains as fine as 0.27µm in these interface regions while the average grain size was approximately 1µm. Additionally, this is the first study to report on the strain rate dependence of AFS IN625 through quasi-static (QS) (0.001/s) and high strain rate (HR) (1500/s) tensile experiments using a servo hydraulic frame and a direct tension-Kolsky bar, respectively, which captured both yield and ultimate tensile strengths increasing as strain rate increased. The HS results exhibited an approximately 200MPa increase in engineering strength over the QS results, with the fracture surfaces at both strain rates aligned with the maximum shear plane and exhibiting localized microvoids.
Avtor
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.