Romankov, S.; Kaloshkin, S.D.; Hayasaka, Y.; Hayashi, N.; Kasai, E.; Komarov, S.V.
Journal of alloys and compounds, 09/2009, Letnik: 484, Številka: 1Journal Article
A vibration technique was used to fabricate Ti–Al coatings. During mechanical milling, the sample surface was subjected to high-energy ball impacts. The powder particles trapped between the balls and substrate became cold-welded to the substrate surface. The repeated substrate-to-ball collisions flattened the particles and forged them onto the surface into a bulk material. The coating thickness and roughness can be optimized by the combinations of key factors such as the ball-to-powder weight ratio, milling duration, and ball size. The development of the coating structure is associated with the milling intensity. A Ti–Al coating formed rapidly as the milling intensity increased. Prolonged milling led to structural refinement of the top coating layer. The grain size may reach the nanometer scale under prolonged milling. The ball size was critical to coating formation.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.