Sadhasivam, S; Rajesh, Narayana Perumal; Ramasamy, P
Journal of alloys and compounds, 05/2014, Letnik: 594Journal Article
Lanthanum doped KTP crystal was grown using high temperature top seeded solution growth technique. The 0.08 wt.% of La super(3+) doping was confirmed by the EDAX analysis. Structural and variation of lattice parameters by doping were investigated by X-ray diffraction. The ferroelectric hysteresis loop was traced in polar axis of grown crystal. Static high frequency dielectric permittivity, suppressed electrical conductivity, low loss tangent, increase of resistivity and modulus properties were studied for lanthanum doped KTP crystal by broad band dielectric spectroscopy. Desirable low ionic conductivity was found as 4 x 10 super(-7) Omega super(-1) cm super(-1) in about 40 kHz frequencies.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.