Kärnfelt, Camilla; Zelenchuk, Dmitry; Sinou, Maïna; Gallée, François; Douglas, Paula
Electronics, 12/2020, Letnik: 9, Številka: 12Journal Article
The creation of hole, cavity or channel structures in low-temperature cofired ceramics (LTCCs), using different sacrificial volume materials (SVMs) was tested. The main functionality of the SVMs should be: easy application into the holes; protection of holes during lamination; uninhibited lamination between layers; and, during firing should burn out before the pores of the LTCCs close, to leave the empty holes clear of any residue. Five different materials were tested—hydroxyethyl cellulose (HEC) 2 wt%, HEC 5 wt%, agar-agar, gelatin, and commercial carbon paste—and compared to a reference sample where no SVMs were used. In all cases, lamination parameters were minimised in order to preserve the tested hole structures. Matrixes with holes ranging from 158 to 268 µm, with pitches of 573 µm in a green state, were tested. The agar-agar caused ceramic deformation as a result of thermal burst during firing and the lamination between the layers was compromised. The carbon paste was difficult to handle, requiring extra equipment for hole filling and incomplete filling of the larger holes. Traces of carbon paste were left as a landing pad on top of the holes, inhibiting lamination at these areas. The gelatin and the 2 wt% and 5 wt% hydroxyethylcellulose (HEC 2 wt% and HEC 5 wt%) filled all holes completely, and also worked as adhesive-assisted lamination (AAL) materials with excellent lamination between layers. Excellent lamination was also observed in the no-SVM case. Thermogravimetric analysis (TGA) and scanning electron microscopy (SEM) with energy-dispersive X-ray (EDX) analyses established that, for all SVMs tested, the remaining residue is negligible after firing. As a result, the HEC 2 wt% material was considered ideal for use as an SVM.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.