Ryzhkova, E.A.; Kolmachikhina, Elvira B.; Dmitrieva, D.V.
Solid state phenomena, 01/2020, Letnik: 299Journal Article
This paper is describing an investigation of sodium lingo-sulfonate and sodium dodecyl-sulfate mixtures influence on zinc concentrates high temperature oxidative pressure leaching and zinc electro-winning. For this purpose, surfactants concentration at leaching tests was varied from 200 to 800 mg∙l-1. It was established that the maximum zinc extraction (99 %) at leaching was achieved in the presence of mixture containing 800 mg∙l-1 lignosulfonate and 200 mg∙l-1 sodium dodecyl-sulfate. Therefore, this mixture can be recommended for high temperature oxidative pressure leaching of zinc concentrates. Sulfur-sulfide pellets formation also was observed at a low lingo-sulfonate concentration (200 mg∙l-1) in a mixture with sodium dodecyl-sulfate. This phenomenon can lead to emergency shut down of autoclave. It was observed that the mixture usage of 800 mg∙l-1 lignosulfonate and 200 mg∙l-1 sodium dodecyl-sulfate had no significant impact on zinc current efficiency, it was in the rage of 92-93 %. The mixture usage of 200 mg∙l-1 lignosulfonate and 600 mg∙l-1 sodium dodecyl-sulfate allowed to increase current efficiency up to 95 %. Increasing sodium dodecyl-sulfate concentration in mixtures with lignosulfonates leads to decrease of current efficiency, to formation of deep pores and defects on cathode zinc surface.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.