This research investigates whether the layup order of the carbon-fibre/glass-fibre skins in hybrid composite sandwich panels has an effect on impact response. Composite sandwich panels with carbon-fibre/glass-fibre hybrid skins were subjected to impact at velocities of 75 ± 3 and 90 ± 3 m s −1 . Measurements of the sandwich panels were made using high-speed 3D digital image correlation (DIC), and post-impact damage was assessed by sectioning the sandwich panels. It was concluded that the introduction of glass-fibre layers into carbon-fibre laminate skins reduces brittle failure compared to a sandwich panel with carbon-fibre reinforced polymer skins alone. Furthermore, if the impact surface is known, it would be beneficial to select an asymmetrical panel such as Hybrid-(GCFGC) utilising glass-fibre layers in compression and carbon-fibre layers in tension. This hybrid sandwich panel achieves a specific deflection of 0.322 mm kg −1  m 2 and specific strain of 0.077% kg −1  m 2 under an impact velocity of 75 ± 3 m s −1 . However, if the impact surface is not known, selection of a panel with a symmetric yet more dispersed hybridisation would be effective. By distributing the different fibre layers more evenly within the skin, less surface and core damage is achieved. The distributed hybrid investigated in this research, Hybrid-(GCGFGCG), achieved a specific deflection of 0.394 mm kg −1  m 2 and specific strain of 0.085% kg −1  m 2 under an impact velocity of 75 ± 3 m s −1 . Blast loading was performed on a large scale version of Hybrid-(GCFGC) and it exhibited a maximum deflection of 75 mm following a similar deflection profile to those observed for the impact experiments.