Alaferdov, A.V.; Savu, R.; Canesqui, M.A.; Kopelevich, Y.V.; da Silva, R.R.; Rozhkova, N.N.; Pavlov, D.A.; Usov, Yu.V.; de Trindade, G.M.; Moshkalev, S.A.
Carbon (New York), April 2018, 2018-04-00, 20180401, Letnik: 129Journal Article
Defects induced by liquid-phase exfoliation of graphite using sonication were studied. It was shown that localized impact by cavitation shock waves can produce bulk ripplocations and various types of dislocations in graphite nanoplatelets. Formation of ripples is more pronounced in large aspect (length/width) ratio platelets or nanobelts. Quasi-periodical ripple systems were observed in many nanobelts after sonication. Mechanism of formation of ripples and dislocations during sonication was proposed. Surprisingly, fast high-temperature processing was found to anneal most of defects. This is consistent with our observations that defects associated with ripplocations are strongly localized and thus can be fast annealed.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.