Yoshimura, R.; Konno, T.J.; Abe, E.; Hiraga, K.
Acta materialia, 06/2003, Letnik: 51, Številka: 10Journal Article
We report here on the early stage of the precipitation behavior of aged Al–Li–Cu alloys using transmission electron microscopy. The δ′ phase (Al 3Li, L1 2 structure (Structurbericht)) was found to exist in the as-quenched specimen containing 2.4 wt%-Li, whereas no precipitation was observed in the as-quenched specimen with 1.6 wt%-Li. After aging at 100 °C for 3 h, GP-I zones nucleated homogeneously in both specimens; but no δ′ phase was detected in the 1.6 wt%-Li alloy at that stage. As the aging proceeds, the δ′ phase nucleates and grows on the GP-I zones. The composite structure, in which the GP-I zone is flanked by a pair of lenticular δ′ particles, is stable in 180–200 °C. The facing lenticular δ′ particles on a GP-I zone were systematically found to be anti-phase with respect to each other.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.