Yablokova, G.; Speirs, M.; Van Humbeeck, J.; Kruth, J.-P.; Schrooten, J.; Cloots, R.; Boschini, F.; Lumay, G.; Luyten, J.
Powder technology, 10/2015, Letnik: 283Journal Article, Web Resource
The growing interest for Selective Laser Melting (SLM) in orthopedic implant manufacturing is accompanied by the introduction of novel Ti alloys, in particular β-Ti for their excellent corrosion resistance as well as favorable combination of high mechanical strength, fatigue resistance and relatively low elastic modulus. As part of the SLM process for producing quality β-Ti parts powder flowability is essential to achieve uniform thickness of powder layers. In this work the flowability of different gas atomized β-Ti, including NiTi, powders has been studied. Their rheological properties were compared to those of commercially available plasma-atomized Ti–6Al–4V powder using a newly developed semi-automatic experimental set-up. Not only the particle size, shape and size distribution of the powders display a large influence on the powder flowability but also particle surface properties such as roughness, chemical composition and the presence of liquid on the surface of the particles. It was found that plasma or gas atomization production techniques for SLM powder have a considerable effect on the particle topography. Among the powders studied regarding SLM applicability only rheological properties of the fine size fraction (25–45μm) of Ti–45Nb didn't conform to SLM processing requirements. To improve flowability of the Ti–45Nb powder it was annealed both in air and argon atmosphere at 600°C during 1h, resulting in an improved rheological behavior suitable for SLM processing. Display omitted •3 novel experimental set-ups were used to study flowability of β-Ti and NiTi powders.•These set-ups prove their relevance for testing powders intended for SLM.•Low flowability of Ti–45Nb gas atomized powder didn't allow SLM processing.•Annealed Ti–45Nb powder showed improved rheological behavior suitable for SLM.•A minimum performance limit below which successful SLM is possible was defined.
Avtor
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.