Lin, Chih-Ming; Hsu, I-Jui; Lin, Sin-Cheng; Chuang, Yu-Chun; Chen, Wei-Ting; Liao, Yen-Fa; Juang, Jenh-Yih
Scientific reports, 01/2018, Letnik: 8, Številka: 1Journal Article
The evolution of iron local vibrational mode (Fe LVM) and phase transitions in n-type iron-doped indium phosphide (InP:Fe) were investigated at ambient temperature. In-situ angle-dispersive X-ray diffraction measurements revealed that InP:Fe starts to transform from zinc-blende (ZB) to rock-salt (RS) structure around 8.2(2) GPa and completes around 16.0(2) GPa. The Raman shift of both transverse and longitudinal optical modes increases monotonically with increasing pressure, while their intensities become indiscernible at 11.6(2) GPa, suggesting that the pressure-induced phase transition is accompanied by significant metallization. In contrast, originally absent at ambient pressure, the Raman shift of Fe LVM appears at ∼420 cm near 1.2 GPa and exhibits a dome shape behavior with increasing pressure, reaching a maximum value of ∼440 cm around 5 GPa, with an apparent kink occurring around the ZB-RS transition pressure of ∼8.5(2) GPa. The Fe K-edge X-ray absorption near edge structure (XANES) confirmed the tetrahedral site occupation of Fe with a crystal field splitting parameter Δ = 38 kJ·mole . Our calculations indicate that the energy parameters governing the phase transition are Δ 0.49 and Δ = 1.10 kJ·mole , respectively, both are much smaller than Δ = 38 kJ·mole at ambient.
Avtor
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.