Hindy, Ahmed; Farahmand, Farzam; Pourdanesh, Fereydoun; Torshabi, Maryam; Al Janabi, A. Hadi; Rasoulianboroujeni, Morteza; Tayebi, Lobat; Tabatabaei, Fahimeh S.
Journal of materials science, 07/2020, Letnik: 55, Številka: 21Journal Article
This study aims to 3D print titanium alloy constructs incorporating gradient of porosities, from the fully dense core to the porous outer surface. Gradient porous specimens were prepared using selective laser melting (SLM). Fully dense specimens fabricated by SLM were used as the control group. Characterization of samples was done using X-ray tomography, uniaxial compression testing, and optical and scanning electron microscopes. The biocompatibility of fabricated samples was investigated using human periodontal ligament stem cells via assessment of cell attachment, viability, and proliferation by direct and indirect assays. The data were analyzed using ANOVA and Tukey’s post hoc test. Characterization of constructs reveals interconnected gradient porosities and higher contact angle in porous samples. The introduction of porosity leads to a significant decrease in compression strength. However, Young’s modulus of the samples with gradient porosity was more similar to the natural bone modulus. The surface microstructure consists of loosely bonded spherical particles. Biocompatibility of the dense and porous samples is appropriate. Although the porosity size led to a reduced cell proliferation rate in the gradient sample, the extract of the gradient sample results in more cell proliferation than the dense sample’s extract. The study demonstrates that a biocompatible functionally graded porous titanium structure can be well fabricated by SLM, and this structure leads to a good match of Young’s modulus to that of the bone.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.