Qin, Yuan; Liu, Ji-Xuan; Li, Fei; Wei, Xiaofeng; Wu, Houzheng; Zhang, Guo-Jun
Journal of advanced ceramics, 03/2019, Letnik: 8, Številka: 1Journal Article
A high-entropy silicide (HES), (Ti 0.2 Zr 0.2 Nb 0.2 Mo 0.2 W 0.2 )Si 2 with close-packed hexagonal structure is successfully manufactured through reactive spark plasma sintering at 1300 °C for 15 min. The elements in this HES are uniformly distributed in the specimen based on the energy dispersive spectrometer analysis except a small amount of zirconium that is combined with oxygen as impurity particles. The Young’s modulus, Poisson’s ratio, and Vickers hardness of the obtained (Ti 0.2 Zr 0.2 Nb 0.2 Mo 0.2 W 0.2 )Si 2 are also measured.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.