Aissani, Linda; Fellah, Mamoun; Chadli, Ablel Hakim; Samad, Mohammed Abdul; Cheriet, Abderrahmane; Salhi, Faiza; Nouveau, Corinne; Weiß, Sabine; Obrosov, Aleksei; Alhussein, Akram
Journal of materials science, 10/2021, Letnik: 56, Številka: 30Journal Article
Magnetron sputtering is one of the most commonly used deposition techniques, which has received considerable attention in industrial applications. In particular, owing to its compatibility with conventional fabrication processes, it can produce and fabricate high-quality dense thin films of a wide range of materials. In the present study, nitrogen (N) was combined with pure vanadium in order to form binary nitride to improve its mechanical and tribological performance. To evaluate the influence of nitrogen on the structure of the as-deposited vanadium nitride (VN) coatings, the following techniques were used: XPS, XRD, SEM, AFM and optical profilometry. The residual stresses were determined by the curvature method using Stoney’s formula. The hardness and Young’s modulus were obtained by nanoindentation measurements. The friction behavior and wear characteristics of the films were evaluated by using a ball-on-disk tribometer. The obtained results showed that the N/V ratio increased with increasing the N 2 flow rate while the deposition rate decreased. The preferred orientation was changed from (200) to (111) as the N 2 flow rate increased with the presence of V–N and V–O binding energies as confirmed by XPS analysis. The nitrogen addition resulted in a columnar morphology and a fine structure with fine surface roughness. The VN thin film containing 49.5 at.% of nitrogen showed the best performance: highest mechanical properties (hardness = 25 GPa), lowest friction coefficient ( μ = 0.37) and lowest wear rate (W s = 2.72 × 10 −5 mm 3 N −1 m −1 ). A good correlation between the film microstructure, crystallite size, residual stress and mechanical and tribological properties was observed.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.