Cologna, Marco; Prette, Andre L. G.; Raj, Rishi
Journal of the American Ceramic Society, February 2011, Letnik: 94, Številka: 2Journal Article
We show that cubic 8 mol% yttria (8YSZ) can be sintered at 750°C with the application of DC electrical fields; in comparison the lowest sintering temperature for 3YSZ was 850°C. Furthermore, cubic zirconia exhibits the onset of flash sintering at 30 V/cm, whereas 3YSZ begins flash sintering at 60 V/cm. However, the volume specific power dissipation for the onset of flash sintering remains similar at ∼10 mW/mm3. The easier sintering of 8YSZ is ascribed to its higher ionic conductivity.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.