Akhtar, Farid; Ogunwumi, Steven; Bergström, Lennart
Scientific reports, 09/2017, Letnik: 7, Številka: 1Journal Article
Thin, binder-less zeolite NaX laminates, with thicknesses ranging between 310 to 750 μm and widths exceeding 50 mm and biaxial tensile strength in excess of 3 MPa, were produced by pulsed current processing. The NaX laminates displayed a high CO adsorption capacity and high binary CO -over-N and CO -over-CH selectivity, suitable for CO capture from flue gas and upgrading of raw biogas. The thin laminates displayed a rapid CO uptake; NaX laminates with a thickness of 310 μm were saturated to 40% of their CO capacity within 24 seconds. The structured laminates of 310 μm thickness and 50 mm thickness would offer low pressure drop and efficient carbon capture performance in a laminate-based swing adsorption technology.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.