Jin, Yu-Juan; Weng, Yun-Xuan; Li, Xue-Xin; Zhang, Min; Xin, Xiu-Lan
Journal of materials science, 01/2015Journal Article
Different proportions of polyamidoamine (PAMAM) dendrimer were blended with poly(hydroxybutyrate-co-hydroxyvalerate) (PHBV) resin in chloroform for film casting. Differential scanning calorimetry and scanning electron microscopy were employed to characterize the PHBV/PAMAM composite films upon stretching and tangential breaking. The results indicated that with the addition of PAMAM dendrimer, the glass transition temperature of the PHBV/PAMAM composite films became more distinct, indicating that the blends had a greater toughness than pure PHBV. The calculated crystallinity values indicated that the crystallinity of the PHBV/ PAMAM blends was lower than that of PHBV (0.09-56.18 % vs. 73.18 %, respectively). Moreover, the mechanical performance tests indicated that the addition of PAMAM dendrimer considerably increased the tangential breaking strength of PHBV from 24.08 kN/m to as high as 62.03 kN/m, whereas the tensile strength remained basically unchanged. The optimal toughening effect was observed with a PAMAM dendrimer content of 3.0 phr.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.