Abdolrahim Davari; Farnaz Farahat; Mahnaz Mehranfar
Journal of dental medicine (Tehran, Iran), 05/2022, Letnik: 35Journal Article
Background and Aims: Recently, the addition of nanoparticles into the restorative materials and tooth preparation by laser for improving the bond strength have been concidered by researchers. The aim of this study was to investigate the shear bond strength of the bioactive glass ionomer containing titanium particles and a conventional glass ionomer with two surface treatments by Er-YAG laser and conventional methods. Materials and Methods: In this in-vitro study, 64 sound extracted premolars were collected. For conventional method, the specimens were prepared in such a way that dentin surfaces with a depth of 0.5 millimeter created at distance of 2 mm from the joint of CEJ at the root or crown. In the laser group, after preparing the teeth, the surface area was prepared by Er-YAG laser. Then, in the middle part of the buccal surface, a cylindrical mold with dimensions of 3.5 mm in diameter and 4 mm in height was placed and for each group was filled with its own glass ionomers. The specimens were divided into 8 groups by simple random sampling (n=8): A (laser, conventional glass ionomer, coronal dentin)/ B (laser, glass ionomer containing titanium nanoparticle, coronal dentin)/C (conventional, conventional glass ionomer, coronal dentin)/ D (conventional, glass ionomer containing titanium nanoparticle, coronal dentin)/ E (laser, conventional glass ionomer, root dentin)/ F (laser, glass ionomer containing titanium nanoparticle, root dentin)/ G (conventional, conventional glass ionomer, root dentin)/ H (conventional, glass ionomer containing titanium nanoparticle, coronal dentin). Finally, the shear bong strength by a universal testing machine was measured at a cross-head speed of 1 mm/min. For data analysis, Two-way ANOVA test was used to evaluate the effect of each variable and their interaction on the shear bond strength and Tukey test was used to compare the two groups. Results: There was significant difference only between groups B with C (P=0.002), E (P=0.007), G (P=0.001) and H (P=0.01). The highest bond strength was found for group B (laser, glass ionomer containing titanium nanoparticle, coronal dentin) and the lowest bond strength for group G (conventional, conventional glass ionomer, root dentin). Conclusion: All three factors of Er-YAG laser, glass ionomer containing titanium nanoparticle and coronal dentin had a positive effect on the improvement of the bond strength.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.