Wang, Xiaodong; Kim, Seong H; Chen, Cheng; Chen, Lei; He, Hongtu; Qian, Linmao
ACS applied materials & interfaces, 07/2015, Volume: 7, Issue: 27Journal Article
The nanowear tests of monocrystalline silicon against a SiO2 microsphere were performed using an atomic force microscope in air as a function of relative humidity (RH = 0%–90%) and in liquid water at a contact pressure of about 1.20 GPa. The experimental results indicated that RH played an important role in the nanowear of the Si/SiO2 interface. In dry air, a hillock-like wear scar with a height of ∼0.4 nm was formed on the silicon surface. However, with the increase of RH, the wear depth on the silicon surface first increased to a maximum value of ∼14 nm at 50% RH and then decreased below the detection limit at RH above 85% or in water. The transmission electron microscopy analysis showed that the serious wear on the silicon surface at low and medium RHs occurred without subsurface damage, indicating that the wear was due to tribochemical reactions between the Si substrate and the SiO2 counter surface, rather than mechanical damages. The RH dependence of the tribochemical wear could be explained with a model involving the formation of “SiOSi” chemical bonds (bridges) between two solid surfaces. The suppression of tribochemical wear at high RHs or in liquid water might be attributed to the fact that the thickness of the interfacial water layer is thick enough to prevent the solid surfaces from making chemical bridges. The results may help us understand the nanowear mechanism of silicon that is an important material for dynamic microelectromechanical systems.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.