Kraner, Jakob; Kim, Kyung Il; Kim, Bonghwan; Kim, Shae K.; Paulin, Irena
Materiali in tehnologije, 01/2023, Volume: 57, Issue: 6Journal Article
The combined effects of the reduction ratio and annealing conditions during cold rolling were investigated for the texture and anisotropy of an EN AW-8011A aluminium alloy. To characterize the microstructural and textural differences, a scanning electron microscope with electron back-scattered diffraction was used. To achieve low anisotropy, the three key factors of texture were exposed: a low fraction of deformed grains according to the average grain misorientation, a large amount of random texture components and the equivalent ratio between deformed and recrystallised texture components. The results of crystallographic texture analysis and anisotropy values revealed that the higher ratio of total cold deformation (cold rolling reduction) and the higher ratio of cold deformation after the intermediate annealing were more favourable for the final continuous annealing in terms of decreasing anisotropy. In contrast, the lower ratio of the cold deformation resulted in lower anisotropy when implementing batch annealing.
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.