Adediran, Adeolu A; Akinwande, Abayomi A; Balogun, Oluwatosin A; Olasoju, O S; Adesina, Olanrewaju S
Scientific reports, 03/2021, Volume: 11, Issue: 1Journal Article
Bamboo fibers (BF) treated in 1.3 Molar NaOH and particulate coconut shell (PCS) sieved to - 45 µm were incorporated into polyvinyl chloride (PVC) matrix towards improving the properties of PVC composite for ceiling boards and insulating pipes which sags and degrade with time needing improvement in properties. The process was carried out via compression moulding applying 0.2 kPa pressure and carried out at a temperature of 170 °C. Composites developed were grouped according to their composition. Groups A, B, C, and D were infused with 2, 4, 6 and 8 wt% PCS at constant amount, respectively. Each group was intermixed with a varying proportions of BF (0-30 wt% at 5% interval). Tests carried out on the samples produced revealed that the yield strength, modulus of elasticity, flexural strength, modulus of rupture were enhanced with increasing BF proportion from 0 to 30 wt% BF at 2 wt% constant PCS input. Thermal and electrical properties trended downward as the fiber content reduced even as the hardness was enhanced with PCS/BF intermix which was also reflected in the wear loss index. Impact strength was highest on the infix of 4 wt% PCS and 15 wt% BF. Compressive strength was better boasted with increasing fiber and PCS amount but 8 wt% PCS amounted to depreciation in trend. It was generally observed that PCS performed optimally at 2 wt% incorporation while beyond that resulted in lowering of strength. Blending of the two variable inputs; 0-30 wt% BF and 2 wt% PCS presented better enhancement in properties.
Shelf entry
Permalink
- URL:
Impact factor
Access to the JCR database is permitted only to users from Slovenia. Your current IP address is not on the list of IP addresses with access permission, and authentication with the relevant AAI accout is required.
Year | Impact factor | Edition | Category | Classification | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Select the library membership card:
If the library membership card is not in the list,
add a new one.
DRS, in which the journal is indexed
Database name | Field | Year |
---|
Links to authors' personal bibliographies | Links to information on researchers in the SICRIS system |
---|
Source: Personal bibliographies
and: SICRIS
The material is available in full text. If you wish to order the material anyway, click the Continue button.