The aim of this study was to investigate the diffusion dynamics of 25% hydrogen peroxide (H2O2) through enamel-dentin layers and to correlate it with dentin’s structural alterations. Micro-Raman ...Spectroscopy (MRS) and Fourier Transform Infrared Photoacoustic Spectroscopy (FTIR-PAS) were used to measure the spectra of specimens before and during the bleaching procedure. H2O2 was applied to the outer surface of human enamel specimens for 60 minutes. MRS measurements were performed on the inner surface of enamel or on the subsurface dentin. In addition, H2O2 diffusion dynamics from outer enamel to dentin, passing through the dentin-enamel junction (DEJ) was obtained with Raman transverse scans. FTIR-PAS spectra were collected on the outer dentin. MRS findings revealed that H2O2 (O-O stretching µ-Raman band) crossed enamel, had a more marked concentration at DEJ, and accumulated in dentin. FTIR-PAS analysis showed that H2O2 modified dentin’s organic compounds, observed by the decrease in amides I, II, and III absorption band intensities. In conclusion, H2O2 penetration was demonstrated to be not merely a physical passage through enamel interprismatic spaces into the dentinal tubules. H2O2 diffusion dynamics presented a concentration gradient determined by the chemical affinity of the H2O2 with each specific dental tissue.
This study evaluated effects of Bioglass 45S5 (BG) and Biosilicate (BS) remineralization on the chemical composition and bond strength of control dentin (CD) and bleached dentin (BD) surfaces.
Dentin ...bleaching treatment was performed using the walking bleaching technique with 0.01 g of sodium perborate and 0.5 mL of 3% hydrogen peroxide for 14 days. Remineralization treatment was carried out by rubbing a remineralization solution (0.015 g of BG or BS diluted in 1.35 mL of distilled water) on the etched dentin surface for 30 seconds. Micro-Raman spectroscopy (MRS) was used to quantitatively analyze the mineral matrix ratios of CD and BD (n=5) after remineralization treatment with BG and BS over 15 days of incubation in artificial saliva. The CD and BD discs (n=10) with and without remineralization treatment with BG and BS were restored using a two-step etch-and-rinse adhesive system (Optibond S, Kerr) and five layers of 1-mm-thick composite resin (Filtek Z250, 3M ESPE). The restored dentin discs were sectioned into nine bonded beams with cross-sectional areas of approximately 0.9 mm
and tested for microtensile bond strength (μTBS). The dentin surface of one fractured beam per tooth was submitted to MRS to characterize the physicochemical composition (n=10) at the interface. The data were analyzed using one-way analysis of variance and the Tukey-Kramer post hoc test (
<0.005).
MRS bioactive analyses revealed that both BG and BS promoted increased mineral matrix ratios in the CD and BD. Significantly higher μTBS values were found after CD treatment with BG (CD: 57 MPa±11; CD-BG: 78 MPa±15) and when BG and BS were applied to the BD (BD: 42 MPa±5; BD-BG: 71 MPa±14; BD-BS: 64 MPa±11) (
<0.005). The MRS analysis of the fractured dentin beam showed that the remineralization treatment significantly increased the dentin relative mineral concentration and promoted the appearance of new interface peaks, indicating a chemical interaction (
<0.005).
Remineralization of BD is an effective therapy to restore damage caused by dentin bleaching and acid conditioning. This approach not only increases dentin mineral compounds but also improves dentin's ability to interact chemically with the adhesive system.
To characterize the chemical interactions and analyze the interface of adhesive systems containing 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) and N-methacryloyl glycine (methacrylamide) ...functional monomers with the dentin in noncarious cervical lesions (NCCLs) compared with artificial defects (ADs).
Twenty human teeth with natural NCCLs on the buccal surface were used. Class V cavities, similar to NCCLs, were created on the lingual surface to serve as controls. Teeth were randomly allocated to two groups according to the functional monomer in the adhesive (N=10): G1, 10-MDP; and G2, methacrylamide. NCCLs and ADs were characterized by their mineral composition (MC) and degree of demineralization (DD) using micro-Raman spectroscopy, adhesive/dentin chemical interactions (CIs) were assessed with infrared photoacoustic spectroscopy, and interface morphology was evaluated with scanning electron and light microscopy. MC, CI, and DD data were submitted to Shapiro-Wilk and Student t-tests ( p<0.05).
Compared with ADs, dentin in NCCLs was hypermineralized ( p<0.05). In G1, CI, and DD in the first 2 μm, and adhesive projections in NCCLs and ADs interfaces were similar. Additionally, a thin layer of dentin collagen was observed in ADs, while it was hardly present in NCCLs. In G2, although CI could not be identified, changes in the mineral components were observed. The DD in the ADs and NCCLs were statistically similar, while SEM showed a lack of adhesion at NCCLs interface. DD and collagen exposure in the ADs and NCCLs were more pronounced than in G1.
Results suggest that the G1 adhesive could be applied directly on the superficial sclerotic layer in NCCLs. In contrast, previous cavity preparation should be conducted to improve the micromechanical interaction of G2 with the dentin.