A single-stage centrifugation method is used for the precipitation and crystallization of a solution of a hybrid halide perovskite compound of the CH
3
NH
3
PbI
3
composition. The perovskite films ...are annealed in the temperature range of 80–140°C, during which the excess of the
N
-methylpyrrolidone solvent was removed by evaporation. The X-ray phase analysis of the synthesized perovskite layer is carried out. The morphology of the surface of the layers after crystallization and the transmission spectra in the optical range are studied. The experiments and research results showed that the optimal temperature regime for the formation and crystallization of lead triiodide methylammonium perovskite films is 100–110°C. The perovskite layers obtained in these processing regimes have a surface morphology with a uniform granular crystal structure and are highly uniform. Moreover, in solar cells based on perovskite-like CH
3
NH
3
PbI
3
structures with an annealing temperature of 100–110°C, the short-circuit currents reached 16.0 mA/cm
2
. At the same time, at annealing temperatures of perovskite layers above 120°С, the maximum value of the short-circuit currents did not exceed 14.0 mA/cm
2
.
Films of anodic aluminum oxide, prepared in an aqueous solution of 0.4 M tartaric acid, are studied by means of electron paramagnetic resonance (EPR) before and after heating at 200–700°C. The ...presence of a carbon radical is established in the films (
g
factor, 2.0027 ± 0.0002). The nature and conditions of its formation during the electrochemical oxidation of aluminum and the heat-treating of anodic aluminum oxide films are discussed.