This paper presents the stabilization effects of the solid extract of kelp (
) on an engineering elastomer, ethylene-propylene copolymer (EPR), which may be used as packaging material. Progressive ...increase in additive loadings (0.5, 1, and 2 phr) increases the oxidation induction time for thermally aged rubber at 190 °C from 10 min to 30 min for pristine material and modified polymer by adding 2 phr protection powder. When the studied polymer is γ-irradiated at 50 and 100 kGy, the onset oxidation temperatures increase as a result of blocking the oxidation reactivity of free radicals. The stabilization effect occurs through the activity of alginic acid, which is one of the main active components associated with alginates. The accelerated degradation caused by γ-exposure advances more slowly when the kelp extract is present. The OOT value for the oxidation of EPR samples increases from 130 °C to 165 °C after the γ-irradiation of pristine and modified (2 phr of kelp powder) EPR, respectively. The altered oxidation state of EPR samples by the action of γ-rays in saline serum is faster in neat polymer than in stabilized material. When the probes are placed in physiological serum and irradiated at 25 kGy, the OOT value for neat EPR (145 °C) is much lower than the homologous value for the polymer samples protected by kelp extract (153 °C for the concentration of 0.5 phr, 166 °C for the concentration of 1 phr, and 185 °C for the concentration of 2 phr).
The thermal and radiation stabilities of POSS modified with various hydrocarbon substituents are studied by chemiluminescence. The material answers are different in relation with the electronic ...densities that exist in the modified structures. The oxidative degradation achieved at four
γ
-doses: 0, 25, 50 and 100 kGy present unlike behavior, because the substituents interact with the frame of silsesquioxanes and the scission of –Si–O–moieties exhibit different levels. The comparison of nonisothermal spectra reveals the generation of hydroperoxides at two different temperatures that demonstrates the induction of degradation by means of the variation of electronic densities.
A series of ethylene-propylene-diene-terpolymer (EPDM)/polyhedral oligomeric silsesquioxane (POSS) composites at different percentage of POSS were prepared and subjected to γ-irradiation. Both ...irradiated and non-irradiated EPDM and composites were investigated by the means of thermal analysis to verify if the presence of POSS molecules is able to reduce the oxidation level of free radicals generated during the degradation and to evaluate the effects of the irradiation. EPDM composites at 1, 3 and 5 mass% of POSS were thus degraded in a thermogravimetric (TG) balance in dynamic heating conditions (25–700 °C), in both inert and oxidative atmosphere by flowing nitrogen and air respectively. Thermal characterization was then completed by carrying out Differential Scanning Calorimetry (DSC) analysis from sub-ambient to better highlight the melting of the polymer and polymer composites occurring just above the room temperature. FTIR spectroscopy was also performed for the prepared samples to check the presence of the molecular filler in the composites and for the TG’s residue at 700 °C, in order to evaluate its nature. DSC and TGA parameters were detected and discussed to have information about the effect of the degradation’s environment, the effect of irradiation on polymer stabilization and the effect of POSS content in the polymer matrix.
This study presents the appropriate solution, algal extracts, for the improvement of polymer durability when the material is subjected to acute oxidation damage. The investigated support, ...styrene-isoprene-styrene (SIS), is modified by three algal extracts:
,
, and
(Kelp) with a low concentration (1 wt%). The presence of polyhedral oligomeric silsesquioxane (POSS) ensures the growth of stability with respect to the pristine polymer. The thermal performances of the host polymer, indicated by chemiluminescence, reveal the essential contribution of an additive to the improvement in oxidation strength. The stability of the polymer adjusted by algal extracts is proved by the activation energy values, which increase from 49 kJ mol
to 89 kJ mol
for the same polymer modified with
. This main important characteristic is the consequence of the highly efficient activity of the polyphenol components of algal extracts and the effect of the three natural additives on the favorably changed kinetic parameters (oxidation induction time and onset oxidation temperature). The exposure of the polymer matrix to the damaging action of γ-rays does not affect the proper contributions to the fast delay in material ageing. The irradiation of 100 kGy, a usual technological dose, may be successfully applied in the radiation processing of a polymer stabilized with algal extracts due to the efficient protection of the additive as the chain-breaking agents.
This study presents the improved stabilization effects of graphene on a polymer substrate, namely a styrene-isoprene-styrene triblock copolymer (SIS) which creates opportunities for long-term ...applications and radiation processing. The added graphene has a remarkable activity on the protection of polymer against their oxidation due to the penetration of free macroradical fragments into the free interlayer space. The chemiluminescence procedure used for the evaluation of the progress of oxidation reveals the delaying effect of oxidative degradation by the doubling extension of oxidation induction time, when the material formulation containing graphene is oxidized at 130 °C. The pristine polymer that is thermally aged requires an activation energy of 142 kJ mol
, while the modified material needs 148, 158 and 169 kJ mol
, for the oxidative degradation in the presence of 1, 2 and, respectively, 3 wt% of graphene. The contribution of graphene content (1 wt%) on the stability improvement of SIS is demonstrated by the increase of onset oxidation temperature from 190 °C for neat polymer to 196 °C in the presence of graphene and to 205 °C for the polymer stabilized with graphene and rosemary extract. The addition of graphene into the polymer formulations is a successful method for enlarging durability instead of the modification of receipt with synthesis antioxidants. The presumable applications of these studied materials cover the areas of medical wear, food packaging, commodities, sealing gaskets and others that may also be included through the products for nuclear power plants.
The EPDM (ethylene-propylene-diene monomer) hybrids with improved thermal and radiation strengths containing 1 and 5 phr of polyhedral oligomeric silsesquioxane (vinyl-POSS, Ov-POSS) and/or 2 phr of ...microalgae (
(
) and
(
)) powders were investigated in respect to their thermal stability after γ-irradiation. The material durability under accelerated degradation was qualified by chemiluminescence and gelation, which prove the contribution of inorganic filler and microalgae extracts on the increase of hybrid thermal stability, as well as the interaction between added components (POSS and
or
). The activation energies and the durabilities under accelerated degradation were calculated, indicating their suitable usage as appropriate materials in various applications. The reported results indicate the improvement effect of both microalgal powders on the oxidation strength, but the contribution of
grabs attention on its efficient effects upon the prevention of degradation under accelerated aging conditions. The thermal performances of the tested EPDM based hybrids are remarkably ameliorated, if the certain formulation includes Ov-POSS (5 phr) and
(2 phr), certifying its suitability for the pertinent applications.
Fluoroelastomers are suitable materials for several applications at high temperature. The present paper presents the modifications of material stability of fluoroelastomer Tecnoflon FOR 80 HS under ...hard operation conditions: thermal and radiation degradation. The sequence of aging stages influences the oxidation state of polymer, which loses its thermal characteristics in the close relation with scission degrees. The chemiluminescence investigation and mechanical testing are the selected procedures for the evaluation of sustained degradation asked for the qualification of O-rings, buffers and gaskets destined to nuclear power plants. The contributions of the two kinds of degrading energies: heat and ionizing radiation are discussed by means of the values of activation energies, which may describe the modification in the oxidation strength. The high temperatures applied in the assessment of material stability (170, 195 and 220 °C) as well as the descendant shape dependencies of the CL intensity vs time indicate the damage tendency with respect to the progress of oxidation in polymer matrix. The large differences between the evolutions of oxidation in the nonisothermal CL spectra of Tecnoflon material depict the existence of different local concentrations of radicals. Their decay takes place over about 100 °C, after which various routes of degradation are followed.
The accelerated degradation of alkyd resins via γ-irradiation is investigated using non-isothermal chemiluminescence. The stability qualification is possible through the comparison of emission ...intensities on a temperature range starting from 100 °C up to 250 °C under accelerated degradation caused by radiolysis scission. The measurements achieved in the samples of cured state resin modified by various inorganic oxides reveal the influence of metallic traces on the aging amplitude, when the thermal resistance increases as the irradiation dose is augmented. Even though the unirradiated samples present a prominent chemiluminescence intensity peak at 80 °C, the γ-processed specimens show less intense spectra under the pristine materials and the oxidation starts smoothly after 75 °C. The values of activation energies required for oxidative degradation of the sample subjected to 100 kGy are significantly higher in the composite states than in the neat resin. The degradation mechanism of polymerized resins is discussed taking into account the effects of fillers on the stability of studied epoxy resin at various temperatures when the degradation and crosslinking are in competition for the decay of free radical.
In this paper several aspects of profound modifications caused by high energy exposures are presented as possible candidates for the efficient adjusting processing of polymer materials. The class of ...hybrid composites receives special attention due to the large spectrum of formulations, where the interphase interaction decisively influences the material properties. They represent potential start points for the intimate uniformity of hybrid morphologies. Their radiation processing turns composites onto hybrid morphology with expected features, because the transferred energy is spent for the modification of components and for their compatibility. The essential changes achieved in radiation processed composites explain the new material behavior and durability based on the peculiar restructuring of polymer molecules that occurred in the polymer phase. During high energy irradiation, the interaction between intermediates born in the constitutive phases may convert the primary composites into hybrids, integrating them into large applicability spheres. During the radiation exposure, the resulting hybrids gain a continuous dispersion by means of new chemical bonds. This type of compounds achieves some specific structural modifications in the polymer phase, becoming stable hybrid composites. The functional properties of hybrids definitely influence the material behavior due to the molecular changes based on the structural reasons. The radiolysis of the vulnerable component becomes an appropriate opportunity for the creation of new material with improved stability. The radiation treatment is a proper conversion procedure by which common mixtures may become continuously reorganized. This review presents several examples for the radiation modifications induced by radiation exposure that allow the compatibilization and binding of components as well as the creation of new structures with improved properties. This approach provides the reference patterns for the extension of radiation processing over the well-conducted adjustments of polymer composites, when certain material features are compulsorily required. From this review, several solutions for the adjustment of regular polymer composites into hybrid systems may become conceivable by the extended radiation processing.
The irradiation consequences on styrene-isoprene-styrene (SIS)/poly(ε-caprolactone) (PCL) blends are discussed starting from the oxidation initiation. Three characterization methods: ...chemiluminescence, differential scanning calorimetry and FTIR spectroscopy are applied. The differences that exist between the two components are revealed, when the oxidation rates of the inspected formulas depend on the blending proportion and the degradation conditions. The relevant activation energies characterizing the oxidation strength as well as the kinetic parameters of degradation during the accelerated damaging of blended polymers are related to the inhibition protection of PCL on the faster oxidation of SIS. The interaction between mixed components is revealed by the structural modifications simultaneously accompanied by the competition of formation and decay of radicals.