Shirasu, N.; Sato, T.; Suzuki, A.; Nagae, Y.; Kurata, M.
Journal of nuclear science and technology, 06/2023, Letnik: 60, Številka: 6Journal Article
Interaction tests between UO 2 and Zr were performed at precisely controlled high temperatures between 1840 and 2000°C (±2.5°C for 1900, 1920, 1930, 1940, and 2000°C, ±10°C for 1840 and 1890°C, respectively), to understand the interaction mechanism in detail. A Zr rod was inserted in a UO 2 crucible and then heat-treated at a fixed temperature in an Ar-gas flow for 10 min. After heating in the range of 1890 to 1930°C, the Zr rod was deformed to a round shape, in which the post-analysis detected the significant diffusion of U into the Zr region and the formation of a dominant α-Zr(O) matrix and a small amount of U-Zr-O precipitates. An abrupt process of liquefaction was observed in the sample heated at around 1940°C or higher. Furthermore, the post-analysis results suggested the detailed liquefaction mechanism: (1) the higher oxygen concentration in the α-Zr(O) matrix suppressed the liquefaction progress, due to the variation in the equilibrium state; (2) the U-Zr-O melt formation progressed by the selective dissolution of Zr from the matrix, corresponding to the reverse variation of the oxygen concentration in the matrix; (3) the selective diffusion of U could occur via the U-Zr-O melt.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.