(Cr2/3Ti1/3)3AlC2 and (Cr5/8Ti3/8)4AlC3: New MAX-phase Compounds in Ti-Cr-Al-C System

E-viri

Recenzirano

(Cr2/3Ti1/3)3AlC2 and (Cr5/8Ti3/8)4AlC3: New MAX-phase Compounds in Ti-Cr-Al-C System

Liu, Zhimou; Zheng, Liya; Sun, Luchao; Qian, Yuhai; Wang, Jingyang; Li, Meishuan

Journal of the American Ceramic Society, 01/2014, Letnik: 97, Številka: 1

Journal Article

Two new MAX compounds, (Cr2/3Ti1/3)3AlC2 and (Cr5/8Ti3/8)4AlC3, were successfully synthesized by hot‐pressing elemental powders at 1500°C for 1 h under 30 MPa in a flowing argon atmosphere. Their crystal structures were indentified and characterized by X‐ray diffraction and transmission electron microscopy analysis. (Cr2/3Ti1/3)3AlC2 and (Cr5/8Ti3/8)4AlC3 have the same crystal structures with the well‐characterized Ti3AlC2 and Ti4AlN3, respectively.

Išči dalje

Avtor

Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.

Leto	Faktor vpliva		Izdaja		Kategorija		Razvrstitev
Leto	JCR	SNIP	JCR	SNIP	JCR	SNIP	JCR	SNIP

Povezave do osebnih bibliografij avtorjev	Povezave do podatkov o raziskovalcih v sistemu SICRIS

Vir: Osebne bibliografije in: SICRIS

Naloži sliko

Vnos na polico

Dodajanje gradiva na polico je uspelo.

Dodajanje gradiva na polico je spodletelo.

Dodajanje gradiva na polico ni bilo potrebno.

Trajna povezava

E-pošta

Faktor vpliva

Izberite knjižnično izkaznico:

Baze podatkov, v katerih je revija indeksirana

Citiranje

Tema