Rapid synthesis of TiC-Fe3C composite by electric discharge assisted mechanical milling of ilmenite (FeTiO3) with graphite

E-viri

Recenzirano

Rapid synthesis of TiC-Fe3C composite by electric discharge assisted mechanical milling of ilmenite (FeTiO3) with graphite

CALKA, A; OLESZAK, D; STANFORD, N

Journal of alloys and compounds, 07/2008, Letnik: 459, Številka: 1-2

Journal Article

Carbo-thermic reduction of ilmenite (FeTiO3) to TiO2 and/or TiC is traditionally carried out by a high temperature annealing treatment at 1500 deg C. In this work, electric discharge assisted mechanical milling (EDAMM) has been used to synthesise TiC + Fe3C from FeTiO3 in 5 min. In this study we report of the reduction of FeTiO3 with C that does not require an additional high temperature annealing treatment.

Išči dalje

Avtor

Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.

Leto	Faktor vpliva		Izdaja		Kategorija		Razvrstitev
Leto	JCR	SNIP	JCR	SNIP	JCR	SNIP	JCR	SNIP

Povezave do osebnih bibliografij avtorjev	Povezave do podatkov o raziskovalcih v sistemu SICRIS

Vir: Osebne bibliografije in: SICRIS

Naloži sliko

Vnos na polico

Dodajanje gradiva na polico je uspelo.

Dodajanje gradiva na polico je spodletelo.

Dodajanje gradiva na polico ni bilo potrebno.

Trajna povezava

E-pošta

Faktor vpliva

Izberite knjižnično izkaznico:

Baze podatkov, v katerih je revija indeksirana

Citiranje

Tema