Adolfi, Dario; Mendes Tribst, João Paulo; Souto Borges, Alexandre Luiz; Bottino, Marco Antonio
The International journal of oral and maxillofacial implants, 03/2020, Letnik: 35, Številka: 2Journal Article
Different titanium bases for implant-supported prostheses can present different mechanical behavior. The goal of this study was to evaluate the torque before and after fatigue, the load to failure, and stress concentration of zirconia restorations cemented or notched to a titanium base. Forty implants were included in polyurethane cylinders and divided into two groups: zirconia restoration cemented on a titanium base and zirconia restoration notched on a titanium base. The specimens had their torque loosening and vertical misfit evaluated before and after cyclic fatigue (200 N/2 Hz/2 × 10 cycles/37°C). Load to failure was evaluated in a universal testing machine (1 mm/min, 1,000 kgf). Failures were evaluated by scanning electron microscopy. Three-dimensional models were created, and the stress concentration was calculated using the finite element method. Data from the in vitro tests were submitted to two-way analysis of variance and Tukey test (α = .5). The cemented restorations presented less torque loosening (19.79 to 15.95 Ncm), lower vertical misfit (3.7 to 10.5 μm), lower stress concentration in the restoration (88.2 to 99.8 MPa), and higher fracture load (451.3 to 390.8 N) than notched restorations. The presence of a cement layer between the restoration and titanium base reduced the susceptibility to abutment screw loosening, improved the resistance to compressive load, and reduced the stress concentration in the restoration.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.