Skobir, Danijela A.; Vodopivec, Franc; Jenko, Monika; Spaić, Savo; Markoli, Boštjan
International journal of materials research, 01/2022, Letnik: 95, Številka: 11Journal Article
The evolution of the chemical and phase composition of carbide precipitates in X20CrMoV12.1 steel after longterm service of 56 000 θ (470 – 530 °C at up to 18MPa) and after heat treatment (650 and 800 °C) was investigated using transmission electron microscopy and Auger electron spectroscopy. The precipitates found were mostly of M type, the S- and v-phase and traces of M C. In service loaded state the presence of M precipitates was also established. The evolution sequence is obviously M C → M !M
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.