Muratova, E. N.; Moshnikov, V. A.; Aleshin, A. N.; Vrublevskii, I. A.; Lushpa, N. V.; Tuchkovskii, A. K.
Glass physics and chemistry, 12/2023, Letnik: 49, Številka: 6Journal Article
A single-stage centrifugation method is used for the precipitation and crystallization of a solution of a hybrid halide perovskite compound of the CH 3 NH 3 PbI 3 composition. The perovskite films are annealed in the temperature range of 80–140°C, during which the excess of the N -methylpyrrolidone solvent was removed by evaporation. The X-ray phase analysis of the synthesized perovskite layer is carried out. The morphology of the surface of the layers after crystallization and the transmission spectra in the optical range are studied. The experiments and research results showed that the optimal temperature regime for the formation and crystallization of lead triiodide methylammonium perovskite films is 100–110°C. The perovskite layers obtained in these processing regimes have a surface morphology with a uniform granular crystal structure and are highly uniform. Moreover, in solar cells based on perovskite-like CH 3 NH 3 PbI 3 structures with an annealing temperature of 100–110°C, the short-circuit currents reached 16.0 mA/cm 2 . At the same time, at annealing temperatures of perovskite layers above 120°С, the maximum value of the short-circuit currents did not exceed 14.0 mA/cm 2 .
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.