Park, Hong-Soo; Yang, In-Mo; Wu, Jong-Pyo; Kim, Myung-Soo; Hahm, Hyun-Sik; Kim, Seong-Kil; Rhee, Hee-Woo
Journal of applied polymer science, 15 August 2001, Letnik: 81, Številka: 7Journal Article
Silicone–acrylic resins were synthesized to prepare superweatherable paints for building materials. The raw materials used were n‐butyl acrylate, methyl methacrylate, and n‐butyl methacrylate as acrylic monomers and 3‐methacryloxypropyltrimethoxysilane (MPTS) as a silicone monomer reactive with the acrylic monomers. Acrylic copolymers were synthesized such that their glass‐transition temperatures were adjusted to 30°C and their MPTS contents were varied to 10, 20, and 30 wt %. As the content of silicone and MPTS increased, average molecular weight and viscosity increased, and thermal stability at high temperatures improved. When we tested the properties of coatings by blending the synthesized silicone–acrylic resins with a white pigment, adhesion was superior with various substrates, and their properties were suitable on the whole. Weatherability was tested by an outdoor exposure test with a weather‐ometer and an accelerated weathering tester, and their results showed that silicone–acrylic resin composed of 30 wt % MPTS was a superweatherable coating. © 2001 John Wiley & Sons, Inc. J Appl Polym Sci 81: 1614–1623, 2001
Avtor
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.