Wang, Yue; An, Ming-zhe; Yu, Zi-ruo; Han, Song; Ji, Wen-yu
Materials and structures, 02/2017, Letnik: 50, Številka: 1Journal Article
The corrosion of reinforcements that results from chloride iron erosion and freeze–thaw damage is the key cause of concrete material failure. Indoor accelerated freeze–thaw cycling tests on reactive powder concrete are carried out in this study, and the mass-loss rate (MLR), relative dynamic-elastic modulus (RDEM), and compressive strength are measured in order to evaluate its durability. In addition, the microstructure and composition of the reactive powder concrete during the chloride-salt freeze–thaw cycles were analyzed using scanning electron microscopy, energy-dispersive spectroscopy, and mercury-intrusion porosimetry. The results show that the reactive powder concrete was durable under chloride freeze–thaw cycling. Furthermore, the values of MLR and RDEM indicated that the actual method is not suitable for reactive powder concrete and should be modified, and that ettringite-type erosion products are generated during the freeze–thaw cycles. The conclusions in this study are valid for specific reactive powder concrete mix.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.