Cheng, Gongjin; Xue, Xiangxin; Jiang, Tao; Duan, Peining
Metallurgical and materials transactions. B, Process metallurgy and materials processing science, 06/2016, Letnik: 47, Številka: 3Journal Article
The effect of TiO 2 on the crushing strength for high-Cr V-Ti magnetite pellets was studied in this paper. On one hand, the crushing strength obviously decreased with the increasing TiO 2 contents. On the other hand, the crushing strength had an obvious increase after grinding treatment for the high-Cr V-Ti magnetite and titanium concentrate. It is found that the crushing strength has great relations with the mineral phase and microstructure. The effect of TiO 2 on the smelting mechanism for high-Cr V-Ti magnetite pellets was also studied in this paper. With the increasing TiO 2 contents in the range of 2.47 to 12.14 pct, the softening start temperature and softening temperature gradually increased, and the softening zone gradually narrowed down; the melting start temperature and the dripping temperature increased, and the melting–dripping temperature zone also increased. The permeability index increased with the increasing TiO 2 contents as a whole. In the process of slag–iron’s dripping and separating, it is proposed that amounts of Cr and V moving to the melted iron are obviously more than those moving to the slag, while amount of Ti moving to slag is much greater than that moving to the melted iron. It is demonstrated that Ti(C,N) generates increasingly with the increasing TiO 2 contents and accumulates as especial regular rigid granules on the surface of coke. The size of melted iron decreased with the increasing TiO 2 contents, and this is in accordance with the present investigations that the dripping difficulty increased with the increasing TiO 2 contents.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.