Sun, W. Z.; Cheng, J. G.; Huang, Z. K.; Jiang, Y.; Wu, L. E.; Liu, L. M.
Journal of materials science, 09/2016, Letnik: 51, Številka: 17Journal Article
When MgO+ZrO 2 were used as a sintering aid to SiC ceramics, it was found that ZrO 2 reacted with SiC and MgO to form ZrC and a magnesium silicate. This reaction may provide a new route to synthesize ZrC or prepare ZrC/SiC composites by reaction sintering using ZrO 2 , SiC, and MgO as starting materials. In the present work, formation process of the ZrC phase in the SiC–MgO–ZrO 2 system was addressed. Subsolidus phase relations at 1550 °C of the SiC–MgO–ZrO 2 system and the related SiC–SiO 2 –ZrC–ZrO 2 –MgO (Si–Zr–Mg–O–C) system were investigated.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.