Toniutti, L.; Mariazzi, S.; Patel, N.; Checchetto, R.; Miotello, A.; Brusa, R.S.
Applied surface science, 10/2008, Letnik: 255, Številka: 1Journal Article
The structural evolution of nanoporous silica thin films was studied by Doppler broadening spectroscopy (DBS), 2–3 gamma ratio of positronium (3γ-PAS) and Fourier transform infrared spectroscopy (FT-IR). Four series of silica films with thickness in the 300–600 nm range were deposited by spin coating on Si substrate changing the content of sacrificial porogen in the sol precursors. The effect on the porosity of different amount of porogen and of the thermal treatments in the 400–900 °C temperature range have been highlighted. The evolution of the porosity is discussed considering the removal of porogen and of the silanol Si–OH groups by thermal treatments as pointed out by FT-IR. Pores with size from less than 1 nm up to sizes larger than 2.0 nm have been detected. In samples with maximum porogen load oPs escaping was observed indicating onset of connected porosity. At temperatures higher than 700 °C a decrease of the porosity due to a progressive pore collapsing was evidenced. A strong correlation was found between the shift of the Si–O–Si transversal optical (TO 3) mode in the FT-IR spectra and the pore size in the porous silica films as revealed by DBS and 3γ-PAS.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.