Xingeng, Li; Jiawen, He
Materials letters, 02/2006, Letnik: 60, Številka: 3Journal Article
Shot blasting on a tube steel of TP304H can greatly improve the oxidation resistance at 650–770 °C in water vapor and an appropriate blasting intensity reached the best result. SEM and EPMA analysis indicated that the structure of the oxide scale turned from multi-layer to monolayer after blasting and Cr 2O 3 is predominant. The untreated sample characterized in multi-layer oxide was composed of Fe in the outer layer and Fe and Cr underneath. For blasted one, the increase of diffusion rate of Cr and the decrease of effective diffusion energy of scale led to a uniform Cr-rich oxide layer, which was dense and protective and the oxidation resistance was increased.
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.