Solis-Romero, J.; Rodríguez-Molina, A.; Solis-Cordova, J.J.; Neville, A.
Materials letters, 07/2022, Letnik: 318Journal Article
•Hydrogenated Diamond-Like Carbon was successfully deposited on AISI 52100 steel.•The multi-layered DLC significantly improved adhesion with 72.6 N of critical load.•The wear rate behaves as the applied load does due to a transferred carbon layer.•Hybrid grey-fuzzy reasoning was used to find optimum real work conditions. The amorphous carbon (a-C:H) coating, with interlayer architectures improves adhesion significantly. Because of this, a novel multi-layered a-C:H coating was deposited on an AISI 52100 steel, by PECVD. The coating was characterised using SEM-EDS, Raman, nano-indentation, interferometry and pin-on-plate. In addition, a designed experiment was implemented for the tribological tests. Wear and friction results were analysed using a hybrid grey-fuzzy method to obtain optimum combination of the tribo-parameters.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.