Roychowdhury, S.; Kain, V.; Gupta, M.; Prasad, R.C.
Corrosion science, 03/2011, Letnik: 53, Številka: 3Journal Article
► Rolled non-sensitised material simulating constrained weldment used for testing. ► Nitrogen (N) in SS 304L adversely affects the IGSCC crack growth rate (CGR). ► Three fold increase in CGR occurred due to increase in N from 0.08 to 0.16 wt.%. ► Increase in CGR attributed to higher yield strength and dynamic strain aging. ► Clear intergranular fracture observed in these experiments. Effect of nitrogen level in strain hardened stainless steel (SS) on crack growth rate (CGR) in simulated boiling water reactor conditions has been the focus of this study. Type 304 LN stainless steel has been used in a warm rolled condition containing two different levels of nitrogen. Clear intergranular (IG) fracture was observed in both the stainless steels. The CGR increased 3 times in the stainless steel with higher level of nitrogen at all levels of dissolved oxygen and this was related to the increase in yield strength due to rolling and dynamic strain aging (DSA).
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.