Abrutis, A.; Plausinaitiene, V.; Skapas, M.; Wiemer, C.; Salicio, O.; Longo, M.; Pirovano, A.; Siegel, J.; Gawelda, W.; Rushworth, S.; Giesen, C.
Microelectronic engineering, 12/2008, Letnik: 85, Številka: 12Journal Article, Conference Proceeding
Films of chalcogenide Ge–Sb–Te materials were grown by pulsed liquid injection chemical vapor deposition (CVD) technique. Simple thermal CVD without additional process activation and CVD with remote activation of precursor decomposition process by a hot-wire were investigated and compared. Ge(NMe 2) 4, Sb(NMe 2) 3 and Te(i-Pr) 2 precursors in a form of diluted solutions in toluene were used for depositions. Film composition was controlled by injection parameters, while the thickness was directly related with number of pulses. Hot-wire activated CVD process allows the growth of chalcogenide films of clearly better quality compared to films grown by standard thermal CVD. Uniform, smooth, crystalline Ge 2Sb 2Te 5 films were grown at substrate/wire temperature 300 °C/550 °C and pressure ⩽ 15 Torr, using nitrogen as a carrier gas, on Si, Si/SiO 2, Si/Si 3N 4 and glass substrates. Forty to forty five nanometer thick films on Si/SiO 2 substrates showed reversible electrical and optical phase switching behavior.
Avtor
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.