Schawe, Jürgen E.K.
Thermochimica acta, 11/2017, Letnik: 657Journal Article
•The initial crystallinity of polymers (αini) is an important property measured by DSC.•The literature proposes a method to determine αini by temperature modulated DSC.•It is shown that this method is not useful for polymer analysis.•Alternative methods by conventional DSC are recommended. The determination of the crystallinity of polymer samples is a typical use of the DSC and it is evaluated from the heat flow curves by various methods A received polymer sample will have an initial crystalline content, which could be zero if the sample was totally amorphous or which is smaller than unity for semicrystalline polymers. The problem with assessing the initial level of crystallinity, is that crystallization may occur during heating, so that the total measured melting enthalpy is the sum of the original amount plus that formed by cold crystallization, for example. Several claims in the literature recommend that the determination of crystallinity can be improved by using temperature modulated DSC (TMDSC). In this contribution we analyze the TMDSC method to determine the initial crystallinity of polymers proposed by Sauerbrunn and Thomas. The conclusion from this result shows that the apparent advantage of the TMDSC technique only arises when a poor baseline selection is made for the evaluation of the DSC curve. It is shown that the method for determination of the initial crystallinity by TMDSC results from incorrect conclusions. The occasionally discussed advantages of this technique are not real. Different techniques for evaluation of conventional DSC curves are referred.
Avtor
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.