Condò, Roberta; Carli, Elisabetta; Cioffi, Alessandro; Cataldi, Maria Elena; Quinzi, Vincenzo; Casaglia, Adriano; Giancotti, Aldo; Pirelli, Paola; Lucarini, Ivano; Maita, Francesco; Maiolo, Luca; Mampieri, Gianluca
Materials, 06/2022, Letnik: 15, Številka: 13Journal Article
Fluoride-based mouthwashes and gels are preventive measures in countering demineralization and caries but, modifying environmental acidity, can reduce the wet corrosion resistance of orthodontic alloys. To evaluate chemical stability, in vitro experiments were conducted on stainless steel and nickel–titanium wires, weighed before and after immersion in household fluorinated mouthwashes and gels, measuring weight variations and elution of metal ions from acid corrosion phenomena. Elution samples were analyzed by inductively coupled plasma mass spectrometry, detecting residual ion concentration, while surface changes were analyzed under scanning electron microscopy. Results showed stainless steel wires do not undergo significant erosion when exposed to most fluorinated mouthwashes but, at prolonged exposure, alloys elute gradually greater amounts of metals and Ni–Ti wires become more sensitive to some mouthwashes. Ions’ elution varies considerably, especially for Ni–Ti wires, if exposed to household fluorinated gels, for which significant negative values were obtained. Changes, affecting wires’ outer layer, negatively act on shiny appearance and luster, reducing corrosion resistance. Although examined orthodontic wires showed good chemical stability and low toxicity, surface corrosion from exposure to fluorinated agents was observed. Home use must be accompanied by clinician prescription and, for household dental gels, must follow manufacturers’ recommendations, ensuring prophylactic action without damaging alloys surfaces.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.