Gorelova, Liudmila A; Pakhomova, Anna S; Krzhizhanovskaya, Maria G; Pankin, Dmitrii V; Krivovichev, Sergey V; Dubrovinsky, Leonid S; Kasatkin, Anatoly V
Journal of physical chemistry. C, 06/2021, Letnik: 125, Številka: 23Journal Article
The high-pressure behavior of slawsonite, SrAl2Si2O8, has been studied using in situ single-crystal X-ray diffraction (SCXRD) and Raman spectroscopy up to 31 GPa. Slawsonite undergoes displacive phase transition between 6 and 8 GPa with the formation of slawsonite-II, featuring fivefold coordinated silicon and aluminum. The results have been confirmed by the changes in vibrational modes using Raman spectroscopy. High-pressure evolution of the Raman spectra of isotypic paracelsian, BaAl2Si2O8, was studied upon compression and decompression up to 37.5 GPa. Raman data for paracelsian upon compression are in good agreement with previously obtained SCXRD data, which demonstrated three phase transitions at ∼6, 28, and 32 GPa with the formation of AlO5, SiO5, AlO6, and SiO6 polyhedra. Raman data upon decompression show the possibility to quench the high-pressure modification, containing AlO5 polyhedra. The comparison of the high-pressure behavior of slawsonite with paracelsian reveals that the increasing size of extra framework cation from Sr2+ to Ba2+ reduces the phase transition pressure but does not change the transformation pathway.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.