Wang, Yiming; Aktaa, Jarir
Scripta materialia, October 2017, Letnik: 139Journal Article
Nano/ultra-fine grained W and W-1wt%La2O3 (80nm–320nm) were fabricated by high-pressure torsion after 2 turns at 300°C/200°C, 400°C, 550°C and 700°C. Distinct textures were observed by using electron backscattering diffraction. Deformed W primarily revealed {112}〈111〉, {110}〈112〉 and {110}〈001〉 components, whereas, deformed W-1wt%La2O3 exhibited mainly γ-fiber at lower process temperatures. The texture anisotropy of (112)1−1−1 and (112)111− pair was also investigated. Results showed that the stacking fault energy and process temperature were crucial in determining texture. Dynamic recrystallization was retarded by La2O3 addition under given conditions. Display omitted
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.