Fukuda, K.; Asakawa, T.; Hamaguchi, R.; Suzuki, T.; Oka, H.; Berghout, Abid; Bechade, Emilie; Masson, Olivier; Julien, Isabelle; Champion, Eric; Thomas, Philippe
Chemistry of materials, 2011, Letnik: 23, Številka: 24Journal Article
We have successfully synthesized the highly c-axis-oriented polycrystals of apatite-type lanthanum silicate by the reactive diffusion technique. When the La2SiO5/La2Si2O7 diffusion couples were isothermally heated at 1773 K - 1873 K for 5 h - 100 h, the apatite polycrystals readily produced in the form of layer at the interfacial boundaries. The annealed couples were characterized using optical microscopy, micro-Raman spectroscopy, X-ray diffractometry and electron probe microanalysis. The product layers were composed of the highly c-axis-oriented prismatic crystallites, with their elongation directions being almost parallel to the diffusion direction. The formation of the apatite layer was controlled by volume diffusion, the overall reaction of which is described by (10+6x)La2SiO5 + (4-3x)La2Si2O7 → 3La9.33+2x(SiO4)6O2+3x (0.01 ≤ x ≤ 0.13). The apatite layer formed at 1873 K was characterized by the steady decrease of the x-value along the diffusion direction from 0.13 at the La2SiO5/apatite interface to 0.01 at the apatite/La2Si2O7 interface. We have also prepared the sandwich-type La2Si2O7/La2SiO5/La2Si2O7 diffusion couples and heated at 1873 K for 100 h. The annealed couple was mechanically processed and the thin-plate electrolyte consisting of the highly c-axisoriented polycrystal was obtained. The oxide-ion conductivity was determined from the impedance spectroscopy data at 573 K - 973 K, which steadily increased from 2.4 × 10-3 S/cm to 2.39 × 10-2 S/cm with increasing temperature. The empirical activation energy of conduction was 0.35 eV, which compares well with the calculated migration energy of 0.32 eV in a previous study.
Avtor
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.