Shlimak, I.; Haran, A.; Zion, E.; Havdala, T.; Kaganovskii, Yu; Butenko, A. V.; Wolfson, L.; Richter, V.; Naveh, D.; Sharoni, A.; Kogan, E.; Kaveh, M.
Physical review. B, Condensed matter and materials physics, 01/2015, Letnik: 91, Številka: 4Journal Article
Raman scattering (RS) spectra and current-voltage characteristics at room temperature were measured in six series of small samples fabricated by means of electron-beam lithography on the surface of a large size (5 x 5 mm) industrial monolayer graphene film. Samples were irradiated by different doses of C super(+) ion beam up to 10 super(15) cm super(-2). It was observed that at the utmost degree of disorder, the Raman spectra lines disappear which is accompanied by the exponential increase of resistance and change in the current-voltage characteristics. These effects are explained by suggestion that highly disordered graphene film ceases to be continuous and splits into separate fragments. The relationship between structure (intensity of RS lines) and sample resistance is defined. It is shown that the maximal resistance of the continuous film is of the order of reciprocal value of the minimal graphene conductivity pih/4e super(2) approximately 20 kOhm.
Avtor
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.