Cocic, Mira; Matovic, Branko; Posarac, Milica; Volkov-Husovic, Tatjana; Majstorovic, Jelena; Tasic, Visa; Devic, Snezana; Vusovic, Nenad
Science of sintering, 2017, Letnik: 49, Številka: 2Journal Article
In this study, the behavior of glass-ceramics synthesized from a glass frit of FFW (Final Flotation Waste) originated from the RTB Bor Company was investigated. Thermal shock resistance was monitored in order to assess the possibility of application of such waste material. Thermal shock of the samples was conducted using water quench test. Image analysis and ultrasonic measurements were used as nondestructive methods for quantification of thermal shock damage at the surface and in the bulk of the specimens. Phase composition of samples was determined by X-ray powder diffraction (XRPD). The degradation level of samples was about 43 % after 20 cycles of water quench tests. The results pointed out that glass-ceramic material exhibited good thermal shock resistance.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.