Nykaza, Jacob R.; Ye, Yuesheng; Elabd, Yossef A.
Polymer (Guilford), 08/2014, Letnik: 55, Številka: 16Journal Article
A polymerized ionic liquid (PIL) diblock copolymer with a long alkyl side-chain, poly(MMA-b-MUBIm-Br), was synthesized at various compositions from an ionic liquid monomer, (1-(2-methacryloyloxy)undecyl-3-butylimidazolium bromide) (MUBIm-Br), and a non-ionic monomer, methyl methacrylate (MMA). The PIL diblock copolymer was synthesized via post-functionalization from its non-ionic precursor PIL diblock copolymer, poly(MMA-b-BrUMA) (BrUMA = 11-bromoundecyl methacrylate), which was synthesized via the reverse addition fragmentation chain transfer (RAFT) polymerization technique. Differential scanning calorimetry reveals two distinct constant glass transition temperatures (Tgs) with a low PIL segment Tg. These PIL block copolymers result in easily processable, flexible, transparent films with high mechanical strength. A high bromide ion conductivity of 64.85 mS cm−1 at 80 °C and 90% RH was measured for the PIL diblock copolymer with an ion exchange capacity (IEC) of 1.44 meq/g (23.3 mol% MUBIm-Br). Interestingly, this result was three times higher than its analogous PIL homopolymer (2.75 meq/g; 100 mol% MUBIm-Br) and an order of magnitude higher than a PIL block copolymer from a previous study with similar chemistry, similar IEC, higher water content, but shorter alkyl side-chain length. Ion conductivity did not scale as expected with water content, which is unusual for water-assisted ion transport (e.g., protons, hydroxide, chloride) in ion-containing polymers, and therefore suggests other mechanisms that impact ion transport in PIL block copolymers. Display omitted
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.