Varga, R.; Ryba, T.; Vargova, Z.; Saksl, K.; Zhukova, V.; Zhukov, A.
Scripta materialia, 10/2011, Letnik: 65, Številka: 8Journal Article
We report on the fabrication, and the magnetic and structural properties of novel glass-coated Ni 50.95Mn 25.45Ga 23.6 microwires with a metallic core diameter of 44 μm and a total diameter of 82 μm prepared by the Taylor–Ulitovsky method. These annealed microwires showed ferromagnetic behaviour with a well-defined easy axis that corresponds to the axis of the wire. X-ray diffraction confirmed a tetragonal martensitic structure with a lattice parameters a = 3.75 Å and c = 6.78 Å. The Curie temperature was estimated to be ∼315 K. The maximum entropy change at the magnetic transition was −0.7 J kg −1 K −1.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.