Hansen, E.; Perret, D.; Bardez-Giboire, I.; Diliberto, S.; Rapin, C.
Journal of non-crystalline solids, 05/2022, Letnik: 584Journal Article
This study investigates the effect of iron oxide Fe2O3 on the homogeneity, viscosity, and glass transition temperature (Tg) of peraluminous glasses. As-quenched glass samples elaborated at 1350 °C show an incorporation limit around 17.5 wt% of Fe2O3 (10.4 mol%), while slowly cooled glass samples show a limit of 7.5 wt% of Fe2O3 (4.2 mol%). Iron in the peraluminous glasses investigated was detected under three configurations: 6-fold coordinated 6Fe3+ in majority, 4-fold coordinated 4Fe3+ and 6-fold coordinated 6Fe2+. It was observed that Fe2O3 addition has a strong fluidifying effect on peraluminous glasses and tends to slightly decrease the glass transition temperature Tg, depending on its thermal history.
![loading ... loading ...](themes/default/img/ajax-loading.gif)
Vnos na polico
Trajna povezava
- URL:
Faktor vpliva
Dostop do baze podatkov JCR je dovoljen samo uporabnikom iz Slovenije. Vaš trenutni IP-naslov ni na seznamu dovoljenih za dostop, zato je potrebna avtentikacija z ustreznim računom AAI.
Leto | Faktor vpliva | Izdaja | Kategorija | Razvrstitev | ||||
---|---|---|---|---|---|---|---|---|
JCR | SNIP | JCR | SNIP | JCR | SNIP | JCR | SNIP |
Baze podatkov, v katerih je revija indeksirana
Ime baze podatkov | Področje | Leto |
---|
Povezave do osebnih bibliografij avtorjev | Povezave do podatkov o raziskovalcih v sistemu SICRIS |
---|
Vir: Osebne bibliografije
in: SICRIS
To gradivo vam je dostopno v celotnem besedilu. Če kljub temu želite naročiti gradivo, kliknite gumb Nadaljuj.